Water Swellable Cement Sheath on Demand, with Sensing Capability

ABSTRACT

A method of sealing propagating cracks in a sensor-laden cement sheath comprising the steps of monitoring an electrical resistivity of the sensor-laden cement sheath to produce a measured value, wherein the sensor-laden cement sheath comprises a conductive sensor, an on-demand expanding agent, and a cement, activating a heat source when the measured value of the electrical resistivity is greater than an activation threshold, increasing a temperature of the sensor-laden cement sheath with the heat source to an activation temperature, wherein the activation temperature is operable to initiate a reaction between the on-demand expanding agent and water, wherein the activation temperature is greater than a formation temperature, reacting the on-demand expanding agent with water to produce a swelled agent, wherein the swelled agent occupies a greater volume than the on-demand expanding agent, and sealing the propagating cracks in the sensor-laden cement sheath with the swelled agent.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority from U.S. Non-Provisional patentapplication Ser. No. 16/570,783, filed on Sep. 13, 2019. For purposes ofUnited States patent practice, this application incorporates thecontents of the Non-Provisional Patent Application by reference in itsentirety.

TECHNICAL FIELD

Disclosed are compositions and methods for use with cement.Specifically, disclosed are compositions and methods for monitoringcement in a downhole environment.

BACKGROUND

The cement sheath in a wellbore annulus, for example, between the casingand the formation wall in a wellbore, impacts the ability to control theflow of formation fluids from the reservoir. Disruptions in the cementsheath, such as radial cracks or microannulus formation, can act as apathway for formation fluid to escape the reservoir in an uncontrolledmanner.

Radial cracks can occur due to downhole stresses from overburdenpressure, completion or fracturing related pressure, or from thermalchanges causing uneven expansion of the casing or cement sheath.Microannulus formation can occur due to shrinkage of the cement sheathor improper displacement of mud.

Identifying the presence of these disruptions and correcting them isimportant to maintain the integrity of the cement sheath. Identificationof some cement sheath disruptions can be directly identified by soniclogging. However, some disruptions, such as small cracks or debondingbetween the cement sheath and rock formation, may not be identifiableusing current technologies. Remediation work to correct the cementsheath disruptions can be expensive. Remedial work can include squeezingmicrofine cement slurry or resins into the cement sheath to seal thecracks.

SUMMARY

Disclosed are compositions and methods for use with cement.Specifically, disclosed are compositions and methods for monitoringcement in a downhole environment.

In a first aspect, a method of sealing propagating cracks in asensor-laden cement sheath is provided. The method includes the steps ofmonitoring an electrical resistivity of the sensor-laden cement sheathto produce a measured value. The sensor-laden cement sheath includes aconductive sensor, an on-demand expanding agent, and a cement. Themethod further includes the steps of activating a heat source when themeasured value of the electrical resistivity is greater than anactivation threshold, such that the measured value that is greater thanthe activation threshold is operable to indicate propagating cracks inthe sensor-laden cement sheath, increasing a temperature of thesensor-laden cement sheath with the heat source to an activationtemperature operable to initiate a reaction between the on-demandexpanding agent and water, where the activation temperature is greaterthan a formation temperature, reacting the on-demand expanding agentwith water to produce a swelled agent, where the swelled agent occupiesa greater volume than the on-demand expanding agent, and sealing thepropagating cracks in the sensor-laden cement sheath with the swelledagent.

In certain aspects, the step of monitoring an electrical resistivity ofthe sensor-laden cement sheath includes the steps of determining ameasured value of an electrical resistivity of the sensor-laden cementsheath, and comparing the measured value of the electrical resistivityto an activation threshold, where the activation threshold is theelectrical resistivity that corresponds to a minimum acceptable amountof propagating cracks in the sensor-laden cement sheath. In certainaspects, the conductive sensor is selected from the group consisting ofcarbon nanotubes, carbon fibers, graphene, metal fibers, andcombinations of the same. In certain aspects, the on-demand expandingagent is selected from the group consisting of magnesium oxide, calciumoxide, and combinations of the same. In certain aspects, the heat sourceis selected from the group consisting of a hot fluid, electricityapplications, resistive heating, microwave applications, andcombinations of the same. In certain aspects, the composition furtherincludes water-filled vesicles. In certain aspects, the on-demandexpanding agent further includes an encapsulation compound. In certainaspects, the encapsulation compound is selected from the groupconsisting of polymeric compounds, ceramic compounds, and combinationsof the same.

In a second aspect, a composition to produce a sensor-laden cementsheath is provided. The composition includes a conductive sensor, theconductive sensor operable to create an electrically conductive network,an on-demand expanding agent, the on-demand expanding agent operable toreact with water, and a cement.

In certain aspects, the composition further includes thermite. Incertain aspects, the composition further includes a metal oxide-typesuper absorber. In certain aspects, the composition further includesencapsulated expanding agents.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other features, aspects, and advantages of the scope willbecome better understood with regard to the following descriptions,claims, and accompanying drawings. It is to be noted, however, that thedrawings illustrate only several embodiments and are therefore not to beconsidered limiting of the scope as it can admit to other equallyeffective embodiments.

FIG. 1A-C provides a pictorial representation of different types ofpropagating cracks.

FIG. 2 provides a pictorial representation of an embodiment of themethod of sealing propagating cracks.

In the accompanying Figures, similar components or features, or both,may have a similar reference label.

DETAILED DESCRIPTION

While the scope of the apparatus and method will be described withseveral embodiments, it is understood that one of ordinary skill in therelevant art will appreciate that many examples, variations andalterations to the apparatus and methods described here are within thescope and spirit of the embodiments.

Accordingly, the embodiments described are set forth without any loss ofgenerality, and without imposing limitations, on the embodiments. Thoseof skill in the art understand that the scope includes all possiblecombinations and uses of particular features described in thespecification.

The compositions and methods are directed to sensor-laden cementcompositions. The sensor-laden cement compositions provide a method forexpanding a sensor-laden cement sheath to minimize or eliminatepropagating cracks in the sensor-laden cement sheath.

Advantageously, the method of sealing propagating cracks in asensor-laden cement sheath can provide a method for real-time monitoringof a propagating crack as the propagating crack expands through thesensor-laden cement sheath. Advantageously, the combination ofconductive sensors and on-demand expanding agent provides the ability totrigger a transformation in the sensor-laden cement sheath.

As used throughout, “electrical resistivity” refers to the degree towhich a material resists the flow of electric current. A low electricalresistivity indicates the material does not resist the flow of electriccurrent. Conversely, a high resistivity indicates the material does notconduct the flow of electric current well.

As used throughout, “percolation threshold” is the minimum amount ofconductive sensors needed to initiate connectivity between theconductive sensors to develop an electron flow path for electricalconductivity.

As used throughout, “propagating cracks” refers to one or more pathwaysin the sensor-laden cement sheath allowing fluid communication betweenthe hydrocarbon-containing formation and the interior of the cement orthe casing. Propagating cracks includes radial cracks, horizontalcracks, micro-annulus formations, and combinations of the same. Thevarious types of propagating cracks can be understood with reference toFIGS. 1A-1C. Radial cracks 100 can occur throughout cement 200surrounding casing 300 appearing as “veining” or “spiderwebbing.”Horizontal cracks 400 can radiate outward from casing 300 as shown inFIG. 1B. Micro-annulus formations 500 can occur when cement 200separates from casing 300 and alternately, when cement 200 separatesfrom formation wall 600.

The sensor-laden cement composition includes a conductive sensor, anon-demand expanding agent, and a cement.

The conductive sensor can be any type of particulate that can bedispersed in cement and can be used to create an electrically conductivenetwork through which an electrical current can flow. The conductivesensors can include carbon nanotubes, carbon fibers, graphene, metalfibers, and combinations of the same. In at least one embodiment, theconductive sensor is carbon nanotubes. Advantageously, by dispersingcarbon nanotube in the sensor-laden cement sheath an electricallyconductive network can be created that behaves as an electro-mechanicalsensor. The conductive sensors are in the absence of encapsulation toensure the conductive sensors are in physical contact with the cement.

The on-demand expanding agent can be any particulate material that canbe dispersed in cement and react with water to produce a swelled agent.The swelled agent occupies a greater volume than the on-demand expandingagent. The particulate material can include organic materials, inorganicparticulates, and combinations of the same.

Organic materials suitable for use as the on-demand expanding agentinclude swellable rubber, water swellable polymers, and combinations ofthe same. Swellable rubber can include natural rubbers and syntheticrubbers. Natural rubbers can include polyisoprene, more specificallycis-1,4-polyisoprene. Synthetic rubbers can include syntheticpolyisoprene, acrylonitrile-butadiene rubber (NBR), carboxylated NBR(XNBR), hydrogenated acrylonitrile-butadiene rubber (HNBR), carboxylatedHNBR (HXNBR), epichlorohydrin rubber (ECO), acrylic rubber (ACM),ethylene-propylene rubber (EPDM), chloroprene rubber, butadiene rubber,styrene-butadiene rubber, fluororubber, silicone rubber, urethanerubber, and isoprene-propylene rubber, and combinations of the same.Water swellable polymers can include polyacrylamide copolymer, ethylenemaleic anhydride copolymer, cross-linked carboxymethylcellulose,polyvinyl alcohol copolymers, crosslinked polyethylene oxide, starchgrafted copolymer of polyacrylonitrile, and combinations of the same.

Inorganic particulates suitable for use as the on-demand expanding agentinclude magnesium oxide, calcium oxide, and combinations of the same.The swelled agent of the inorganic particulates can include magnesiumhydroxide (Mg(OH)₂), calcium hydroxide (Ca(OH)₂), and combinations ofthe same. The inorganic particulates suitable for use as the on-demandexpanding agent can be present in different reactive grades. Thereactive grade of the inorganic particulates can be due to themanufacturing calcination temperature. The greater the manufacturingcalcination temperature the greater the degree of crystallinity and thelower the reactivity. The reactivity can influence the activationtemperature of the reaction between the on-demand expanding agent andthe water. In at least one embodiment, the on-demand expanding agent canbe include a combination of types of inorganic particulates. In at leastone embodiment, the on-demand expanding agent can include one type ofinorganic material selected from across different reactive grades. In atleast one embodiment, the on-demand expanding agent can include acombination of types of inorganic particulates with different reactivegrades included for each type of inorganic particulates. The specifictypes and reactive grades of the inorganic particulates suitable for useas the on-demand expanding agent can be selected for a specificactivation temperature. Advantageously, selecting a combination of typesof inorganic particulates with a range of reactive grades can allow thereaction period to be tailored. Tailoring the reaction period can resultin a reaction that extends for the desired length of time andalternately, in a reaction period that can be stopped and restarted asneeded.

In at least one embodiment, the on-demand expanding agent can includeboth inorganic particulates and organic materials.

The on-demand expanding agents can be encapsulated with an encapsulationcompound to produce an encapsulated expanding agent. The encapsulationcompound can be any type of material suitable for encapsulating theon-demand expanding agent and delaying the interaction between water andthe on-demand expanding agent. In at least one embodiment, theencapsulation compound can be permeable or semi-permeable to water, suchthat water permeates through the encapsulation compound and interactswith the on-demand expanding agent within the encapsulation compound. Inat least one embodiment, the encapsulation compound can degrade, suchthat the on-demand expanding agent is exposed to water as theencapsulation compound degrades. The encapsulation compound can includepolymeric compounds, ceramic compounds, polymer-ceramic compositecompounds, and combinations of the same. Polymeric compounds suitablefor use as the encapsulation compound include cellulosic-type polymers,degradable polymers such as polylactic acid, thermoplastic-typepolymers, latex-type polymers, and combinations of the same. Ceramiccompounds suitable for use as the encapsulation compound can includezirconia, silicon nitride, silicon carbide, and combinations of thesame. The encapsulation compound can be selected to provide control overthe reaction kinetics of the on-demand expanding agents, activationenergy, and reactivity. By delaying the interaction between water andthe on-demand expanding agent, the encapsulation can delay the reactionof the on-demand expanding agents with water. Advantageously, theencapsulation compound can provide additional flexibility and elasticityto the sensor-laden cement composition and the sensor-laden cementsheath. Advantageously, the encapsulation compound can act as a fillerin the sensor-laden cement composition and the sensor-laden cementsheath.

In embodiments, where the encapsulation compound is a polymericcompound, the encapsulated expanding agent can be produced according tothe following method. The polymeric compound can be heated to atemperature greater than its glass transition temperature to produce asoftened polymeric compound. The on-demand expanding agent can be mixedwith the softened polymeric compound to produce a dispersed polymericmixture, such that in the dispersed polymeric mixture the on-demandexpanding agent is dispersed throughout the softened polymeric compound.The dispersed polymeric mixture is reduced to a temperature less thanthe glass transition temperature of the polymeric compound to produce acooled dispersion. The cooled dispersion can be ground to produce theencapsulated expanding agents, such that the grinding can produceencapsulated expanding agents of the desired particle size.

In at least one embodiment, the sensor-laden cement composition caninclude on-demand expanding agents. In at least one embodiment, thesensor-laden cement composition can include encapsulated expandingagents. In at least one embodiment, the sensor-laden cement compositioncan include a combination of on-demand expanding agents and encapsulatedexpanding agents.

The cement can be any cement suitable for use in a wellbore cementingoperation. Suitable cements are those that can undergo a curing processto produce a cement sheath.

The water-filled vesicles can be any type of component capable ofholding water in a cement composition. The water-filled vesicles caninclude an outer shell surrounding a droplets of water. The outer shellcan be formed of any material capable of storing and releasing water.Examples of materials suitable for use as the outer shell can includecellulose, super absorbing polymers, and combinations of the same. Superabsorbing polymers are also known as super absorbent polymers. In atleast one embodiment, the water-filled vesicles can include the dropletsof water when the water-filled vesicles are mixed with the sensor-ladencement composition. In at least one embodiment, the water droplets canenter the water-filled vesicles as the cement cures to produce thesensor-laden cement sheath. The water-filled vesicles can provide aninternal source of water for the reaction with the on-demand expandingagents. In at least one embodiment, the sensor-laden cement sheath is inthe absence of sufficient water to react with the on-demand expandingagents and water can flow from the water-filled vesicles to the curedcement sheath and act as a reactant. In at least one embodiment, wherethe outer shell is composed of cellulose, the cellulose can degrade atthe activation temperature and release the water into the sensor-ladencement sheath. As water in the surrounding cement is depleted, the watercan be drawn from water-filled vesicles into the surrounding cement.

In at least one embodiment, the sensor-laden cement composition caninclude thermite, such that the thermite can be dispersed and embeddedin the sensor-laden cement sheath. The thermite can be encapsulated bythe encapsulation compound. In at least one embodiment, metal oxide-typesuper absorbers can be mixed with the sensor-laden cement composition,such that the metal oxide-type super absorbers are dispersed andembedded throughout the sensor-laden cement sheath. In at least oneembodiment, the metal oxide-type super absorber can be an iron oxideparticle.

A method of preparing the sensor-laden cement composition is described.In one method of preparing the sensor-laden cement composition, theconductive sensors can be mixed with water to produce asensor-containing water. Advantageously, mixing the conductive sensorswith water before the cement can minimize air pollution by reducing theamount of nanoparticles that are released in the air. In at least oneembodiment, the sensor-containing water can be subjected to sonicationto separate the conductive sensors and increase the uniformity of thesensor-containing water. The on-demand expanding agents can be mixedwith the cement to produce an agent-cement mix. The agent-cement mix canthen be mixed into the sensor-containing water to produce thesensor-laden cement composition. In alternate method of preparing thesensor-laden cement composition, the conductive sensors can be mixedwith water to produce a sensor-containing water and then the on-demandexpanding agents can be mixed with the sensor-containing water toproduce a sensor-agent water mixture. Mixing the on-demand expandingagents with the sensor-containing water can increase the amount of waterabsorbed by the on-demand expanding agents. Then the cement can be mixedwith the sensor-agent water mixture to produce the sensor-laden cementcomposition. The sensor-agent water mixture can be prepared inembodiments where the on-demand expanding agents can be exposed to waterbefore being mixed with the cement.

The conductive sensors can be present in the sensor-laden cementcomposition at a concentration not greater than 1 percent by weight ofcement (% BWOC), alternately between 0.1% BWOC and 1% BWOC, andalternately between 0.1% BWOC and 0.99% BWOC. The concentration ofconductive sensors in the sensor-laden cement composition is based onthe need to cross a percolation threshold for a conductive network.Concentrations greater than 1% BWOC would not have an impact on theconductive network. The on-demand expanding agents can be present in thesensor-laden cement composition at a concentration between 8% BWOC and25% BWOC, alternately between 10% BWOC and 25% BWOC, alternately between10% BWOC and 15% BWOC, alternately between 15% BWOC and 20% BWOC, andalternately between 20% BWOC and 25% BWOC.

A method of producing a sensor-laden cement sheath is described. In afirst step, the sensor-laden cement composition can be used in any typeof cementing operation undertaken in a wellbore. The wellbore cantraverse a hydrocarbon-containing formation, such that the wellboreprovides fluid communication between the hydrocarbon-containingformation and the surface. The sensor-laden cement composition can bepumped into an annulus of a wellbore between a casing and the formationwall and alternately into an annulus of a wellbore between two casingstrings. The step of pumping the sensor-laden cement composition intothe annulus can include the equipment and steps standard for introducinga standard cement composition into an annulus of a wellbore.

The sensor-laden cement composition is then allowed to cure under thecuring conditions to produce the sensor-laden cement sheath. The curingconditions can include temperature, moisture content, cure period, andcombinations of the same. The curing conditions can be in the same rangeas a standard wellbore cement in the absence of conductive fibers oron-demand expanding agents. The curing conditions can be selected basedon the conditions in the wellbore, the type of cement selected, and thedesired final properties of the sensor-laden cement sheath.

A method of sealing propagating cracks in a sensor-laden cement sheathis provided. In a first step, the electrical resistivity is monitored.The electrical resistivity can be monitored in real-time and in-situ.The electrical resistivity can be monitored at any interval suitable forproviding the desired data and can be based on the properties of thesensor-laden cement sheath and the wellbore conditions.

During the step of monitoring the electrical resistivity, a measuredvalue of an electrical resistivity of the sensor-laden cement sheath canbe determined. Any method useful for determining a measured value of theelectrical resistivity of a material can be used. The measured value ofthe electrical resistivity of the sensor-laden cement sheath provides anindirect measure of the mechanical stress and strain in the sensor-ladencement sheath, which cannot be directly measured. In at least oneembodiment, the electrical resistivity is measured using transmittingelectrodes and receiving electrodes in electrical connection with thesensor-laden cement sheath. The transmitting electrodes and receivingelectrodes can be attached to the casing before the sensor-laden cementis introduced to the wellbore. The transmitting electrodes and receivingelectrodes can be any type of conductor through which electricity canenter or exit the sensor-laden cement sheath. A current can beintroduced through one or more of the transmitting electrodes. Becausethe conductive sensors are in physical contact with the cementthroughout the sensor-laden cement sheath the introduced current cantravel through the conductive sensors to one or more of the receivingelectrodes. The receiving electrodes can detect the current and send asignal to the surface. The measure of electrical resistivity can bedetermined by measuring the electrical resistance and the impedance. Thesignal strength can be related to the applied voltage, the intrinsicrestivity of the material, and the detected damages. The measurementscan be detected on the time frame of a fraction of a second. Theconductive sensors enhance the introduced current and enable the in-situmeasurement of the stress and strain on the sensor-laden cement sheath.Without being bound to a particular theory, the propagating cracksdisrupt the network produced by the conductive sensors dispersed in thesensor-laden cement sheath resulting in a weaker current being sensed bythe receiving electrodes. Advantageously, the step of determining ameasured value of an electrical resistivity of the sensor-laden cementsheath can be performed in real-time and continuously. The specificinterval at which current is introduced through one or more of thetransmitting electrodes can be determined based on the wellboreconditions and the properties of the sensor-laden cement sheath.

In a second step of monitoring the electrical resistivity, the measuredvalue of the electrical resistivity can be compared to an activationthreshold for the sensor-laden cement sheath. The activation thresholdcan be a value for the electrical resistivity of the sensor-laden cementsheath based on laboratory testing of the specific sensor-ladencomposition allowed to cure under the cure conditions for the desiredwellbore and the conditions of the wellbore. The activation threshold isthe electrical resistivity that corresponds to the minimum acceptableamount of propagating cracks in the sensor-laden cement sheath. Theactivation threshold provides a qualitative measure of the propagatingcracks. A measured value that is less than the activation thresholdindicates the amount of propagating cracks is less than the minimumacceptable amount. A measure of the electrical resistivity that isgreater than the activation threshold indicates the amount ofpropagating cracks is greater than the minimum acceptable amount. Thecomparison of the measured value to the activation threshold can be doneby hand or can be done by computer. Advantageously, the use ofconductive sensors enables the real-time, in-situ evaluation of themechanical stress and strain in the sensor-laden cement sheath. In atleast one embodiment, the comparison of the measured value to theactivation threshold is performed continuously and concurrently with thestep of determining a measured value of the electrical resistivity ofthe sensor-laden cement sheath. While the measured value is less thanthe activation threshold no further steps are taken and the step ofmonitoring the electrical resistivity can continue.

When the measured value is greater than the activation threshold, theheat source can be activated. The heat source can be any source suitableto produce heat such that the heat can increase a temperature of thesensor-laden cement sheath to an activation temperature. The heat sourcecan be a direct heating source or an indirect heating source. Examplesof sources suitable to produce heat include a hot fluid, electricityapplications, resistive heating, microwave applications, andcombinations of the same.

Hot fluids can be introduced to the inner casing of the wellbore, wherethe heat from the hot fluids can radiate through the casing to thesensor-laden cement sheath and then through the sensor-laden cementsheath. Examples of hot fluids include hot liquids and steam. Thetemperature of the hot fluids can be determined based on the desiredactivation temperature. Advantageously, hot fluids are common on a wellsite and the temperature can be adjusted to the desired activationtemperature.

Electricity applications can include activating an electric network andinitiating thermite reactions. Activating an electric network can useelectricity to activate the electric network formed by the conductivesensors dispersed in the sensor-laden cement sheath. Applyingelectricity to produce an electric field in the sensor-laden cementsheath can generate heat due to the Joule effect. The current applied toactivate the electric network is greater than the current applied tomeasure the electrical resistivity. Advantageously, applying electricityto increase the temperature to the activation temperature uses the samesystem that is used to measure the electrical resistivity. Initiatingthermite reactions can use electricity to ignite thermite resulting inan exothermic reduction-oxidation reaction. The thermite can bedispersed in the fluids in the casing, alternately dispersed in thesensor-laden cement sheath, and alternately delivered by wireline to thefluids in the casing of a targeted zone. The heat produced by theexothermic reduction-oxidation reaction of thermite in the fluids in thecasing can increase the temperature of fluids, such that heat flowsthrough the casing and into the sensor-laden cement sheath. The heatproduced by the exothermic reduction-reaction can increase thetemperature of the sensor-laden cement sheath surrounding the thermite.

Resistive heating can use an electrical heating coil deployed viawireline tools to heat the fluid in the casing at a targeted zone. Theheat can flow from the fluid through the casing and into thesensor-laden cement sheath. By controlling the size of the electricalheating coil and the location in the casing where it is deployed, theuse of resistive heating can increase the temperature of sensor-ladencement sheath in only the targeted zone. Heating the sensor-laden cementsheath in targeted zones provides better control of the reactions of theon-demand expanding agents, by limiting the section of the sensor-ladencement sheath where the reactions occur.

A microwave source can be deployed in the casing via wireline tools,such that the microwave source produces microwave energy in a targetedzone. In at least one embodiment, the microwave energy can heat fluidsin the casing at the targeted zone. The heat flows from the fluidthrough the casing and into the sensor-laden cement sheath. In anembodiment using metal oxide-type super absorbers in the sensor-ladencement sheath, the microwave energy can be absorbed by the metaloxide-type super absorber and increase the temperature of the metaloxide-type super absorbers. The heat can flow from the metal oxide-typesuper absorbers to the sensor-laden cement sheath and increase atemperature of the sensor-laden cement sheath. In an embodiment usingmetal oxide-type super absorbers and a microwave source, the casing canbe fully or partially transparent to microwave energy. Using a microwavesource to produce microwave energy in a targeted zone can allow forbetter control of the reactions the on-demand expanding agents, bylimiting the section of the sensor-laden cement sheath where thereactions occur.

Applying a combination of heat sources can be used to control thereaction time, the time for heating, the location of the targeted zone,the number of targeted zones, and a combination of the same. Thespecific heat source selected can be based on the desired increase intemperature, the time for heating, the location of the targeted zone,the number of targeted zones, and combinations of the same.

The activation temperature is the temperature at which the reactionbetween the on-demand expanding agents and water is initiated. Theactivation temperature is determined by the composition of the on-demandexpanding agent, including the types of particulate material, thedifferent reactive grades for the types of particulate material, and thepresence of encapsulated expanding agents. The activation temperature isgreater than a formation temperature to ensure the reaction between theon-demand expanding agent and water is initiated by activating the heatsource and not due to the ambient temperature of the sensor-laden cementsheath before the heat source is activated.

In embodiments that include the use of encapsulated expanding agents,where the encapsulation compound degrades, the activation temperaturecan be the temperature at which the encapsulation compound degrades.After the encapsulation compound degrades, the on-demand expanding agentcan be exposed to the activation temperature. In at least oneembodiment, a first activation temperature can be the temperature atwhich the encapsulation compound degrades and a second activationtemperature can be the temperature to trigger the expanding agent, wherethe first activation temperature is less than the second activationtemperature.

After the temperature of the sensor-laden cement sheath is increased tothe activation temperature, the reaction between the on-demand expandingagent and water is initiated. The water can be the water present in thepores of the sensor-laden cement sheath or can be from the water-filledvesicles. The reaction between the on-demand expanding agent and watercan produce the swelled agent. The swelled agent can occupy a greatervolume than the on-demand expanding agent occupied.

The swelled agents can seal the propagating cracks by filling the spaceof the propagating cracks and alternately can apply a force in thesensor-laden cement sheath causing the cement in the sensor-laden cementsheath to move to fill the space of the propagating cracks.

The method for sealing propagating cracks is illustrated in FIG. 2 .Encapsulated expanding agents 10 are dispersed throughout thesensor-laden cement sheath 20 along with water-filled vesicles 30.Encapsulated expanding agents 10 include on-demand expanding agents 12and encapsulation compound 14. Propagating crack 40 occurs betweencasing wall 50 and sensor-laden cement sheath 20. When the measuredvalue is greater than the activation threshold, heat source 60 isactivated. As a result of heat source 60 being activated, thetemperature in sensor-laden cement sheath 20 is increased to theactivation temperature and the encapsulated expanding agents 10 reactwith water from the sensor-laden cement sheath 20 or water-filledvesicles 30 to produce swelled agents 70. Swelled agents 70 expandforcing sensor-laden cement sheath 20 toward casing wall 50 sealing thepropagating crack.

Although the embodiments have been described in detail, it should beunderstood that various changes, substitutions, and alterations can bemade hereupon without departing from the principle and scope.Accordingly, the scope of the embodiments should be determined by thefollowing claims and their appropriate legal equivalents.

There various elements described can be used in combination with allother elements described here unless otherwise indicated.

The singular forms “a”, “an” and “the” include plural referents, unlessthe context clearly dictates otherwise.

Optional or optionally means that the subsequently described event orcircumstances may or may not occur. The description includes instanceswhere the event or circumstance occurs and instances where it does notoccur.

Ranges may be expressed here as from about one particular value to aboutanother particular value and are inclusive unless otherwise indicated.When such a range is expressed, it is to be understood that anotherembodiment is from the one particular value to the other particularvalue, along with all combinations within said range.

As used here and in the appended claims, the words “comprise,” “has,”and “include” and all grammatical variations thereof are each intendedto have an open, non-limiting meaning that does not exclude additionalelements or steps.

The invention claimed is:
 1. A composition to produce a sensor-ladencement sheath, the composition comprising: a conductive sensor, theconductive sensor operable to create an electrically conductive network;an on-demand expanding agent, the on-demand expanding agent operable toreact with water; and a cement.
 2. The composition of claim 1, whereinthe conductive sensor is selected from the group consisting of carbonnanotubes, carbon fibers, graphene, metal fibers, and combinations ofthe same.
 3. The composition of claim 1, wherein the on-demand expandingagent is selected from the group consisting of magnesium oxide, calciumoxide, and combinations of the same.
 4. The composition of claim 1,further comprising water-filled vesicles.
 5. The composition of claim 1,further comprising thermite.
 6. The composition of claim 1, furthercomprising a metal oxide-type superabsorber.
 7. The composition of claim1, further comprising encapsulated expanding agents.